RP Graphite Electrode
Raw materials are mixed and then molded. Heat treatment is then applied in the baking and graphitization process to form the finished product.
- Product Details
Physical & Chemical Properties of RP Graphite Electrodes
|
Items |
Classification |
Unit |
Nominal Diameter (mm) |
|||||||||
|
75-130 |
150-225 |
250-300 |
350-450 |
500-800 |
||||||||
|
Grade A |
Grade B |
Grade A |
Grade B |
Grade A |
Grade B |
Grade A |
Grade B |
Grade A |
Grade B |
|||
|
Resistivity |
Electrode |
μΩm |
8.5 |
10.0 |
9.0 |
10.5 |
9.0 |
10.5 |
9.0 |
10.5 |
9.0 |
10.5 |
|
Nipple |
8.0 |
8.0 |
8.0 |
8.0 |
8.0 |
|||||||
|
Bending Strength |
Electrode |
Mpa |
10.0 |
10.0 |
8.0 |
7.0 |
6.5 |
|||||
|
Nipple |
15.0 |
15.0 |
15.0 |
15.0 |
15.0 |
|||||||
|
Young’s Modulus |
Electrode |
Gpa |
9.3 |
9.3 |
9.3 |
9.3 |
9.3 |
|||||
|
Nipple |
14.0 |
14.0 |
14.0 |
14.0 |
14.0 |
|||||||
|
Bulk Density |
Electrode |
g/cm3 |
1.58 |
1.53 |
1.53 |
1.53 |
1.52 |
|||||
|
Nipple |
1.70 |
1.70 |
1.70 |
1.70 |
1.70 |
|||||||
|
CTE (100℃-600℃) |
Electrode |
×10-6/℃ |
2.9 |
2.9 |
2.9 |
2.9 |
2.9 |
|||||
|
Nipple |
2.7 |
2.7 |
2.8 |
2.8 |
2.8 |
|||||||
|
Ash Content |
|
% |
0.5 |
0.5 |
0.5 |
0.5 |
0.5 |
|||||
Note: Ash Content is only for reference.
Recommended current load of RP Graphite Electrodes
|
Grade |
Nominal Dia. |
Allowable current A |
Current density A/cm2 |
|
RP electrode |
200mm |
500～6900 |
15～21 |
|
250mm |
7000～10000 |
14～20 |
|
|
300mm |
10000～13000 |
14～18 |
|
|
350mm |
13500～18000 |
14～18 |
|
|
400mm |
18000～23500 |
14～18 |
|
|
450mm |
22000～27000 |
13～17 |
|
|
500mm |
25000～32000 |
13～16 |
|
|
550mm |
28000～34000 |
12～14 |
|
|
600mm |
30000～36000 |
11～13 |
|
|
650mm |
32000～39000 |
10～12 |
|
|
700mm |
34000～42000 |
9～11 |
Related Products
HP Graphite Electrode
Physical & Chemical Properties of HP Graphite Electrodes ...
SHP Graphite Electrode
Physical & Chemical Properties of SHP Graphite Electrodes...
Soderberg Electrodes Paste
Soderberg Electrode Paste is also called Anode Paste, Self-baking Electrodes Paste or Electrode...